Key features

• Ready to use - no mixing, applied from cartridge
• Solvent free
• Completely non-sagging
• Tough and flexible after curing
• Cures by moisture absorption from air
• Service temperature -60 to +180 C
• Up to 95% recovery after plastic deformation
• Good UV resistance and insulation properties
• Self priming on glass, ceramics and vitreous surfaces

Applications

• Sealing glass and aluminium and non-oily wood
• Sealing aluminium/glass window frame joints
• Fixing glass into aluminium frames in lieu of rubber beading

Specifications

Chemistry: Acetoxy cure single-component silicone | Appearance: Thick uniform thixotropic paste free from bubbles | Density: 0.94 - 1.00 g/cc | Skinning time: 5.0 - 25 minutes | Tack free time: Maximum 40 minutes | Hardness: 15 - 25 Shore A | Extrusion rate: Minimum 2.0 g/sec | Slump (vertical/horizontal): Max. 2 mm | Curing time: Approximately 24 hrs for 1-1.5 mm at 25 C | Tensile strength at break (ASTM D 412): Min 0.5 N/sq.mm | Elongation at break (ASTM D 412): Min. 375 % | Service temperature: -60 to +180 C | Coverage (one 240 ml cartridge): 9.6 linear m for 5x5 mm joint; 2.4 linear m for 10x10 mm joint | Shelf life: 12 months from manufacture | Full cure: 7 days minimum above 50% RH

Packing: 280 ml & 240 ml plastic cartridge with separate nozzle