Key features

• Ready to use - no mixing
• Completely non-sagging
• Tough and flexible after curing
• Elastomeric from -40 C to +150 C
• Good UV resistance
• Self-priming - primerless adhesion to most porous and non-porous materials
• Compliant with ISO 11600 F 20HM

Applications

• Sealing glass, aluminium, non-oily wood, brick, concrete, steel, ceramic, selected plastics
• Aluminium/glass window frame joints and fixing glass into aluminium frames in lieu of rubber beading
• Expansion joints, metal curtain walls, modular components
• General glazing and perimeter weatherproof sealing

Specifications

Skin formation time Clear / White / Black: 5-20 / 10-20 / 10-20 min | Tack free time (ASTM C 679): <40 min | Sag/slump vertical (ASTM D 2202): < 2 mm | Full cure time: 7-14 days | Hardness Shore A (ASTM C 661) Clear / White / Black: 22 / 30 / 30 | Tensile strength (ASTM D 412) Clear / White / Black: >=0.8 / 1.5 / 1.5 N/mm2 | Elongation at break Clear / White / Black: 800 / 900 / 900 % | Tear strength Die C (ASTM D 624) Clear / White / Black: 4 / 7 / 7 N/mm | Service temperature: -40 to +150 C | Coverage (280 ml cartridge): 7.7 linear m for 6x6 mm joint; 2.8 linear m for 10x10 mm joint | Shelf life: 12 months from manufacture | Full cure: 7 days minimum above 50% RH

Standards: ISO 11600 F 20HM

Packing: 280 ml plastic cartridge with separate nozzle; White, Clear, Black