Key features

• Extremely fast application: tack free in seconds, walk on in minutes
• Seamless waterproofing
• Excellent adhesion to concrete, steel, aluminium, wood, foam
• Can transgress multiple substrate types in one application
• No protector boards needed when back filling
• 100% solids, VOC-free, solvent free
• Good abrasion and impact resistance
• Excellent thermal stability
• Rapid return to service

Applications

• Large scale waterproofing for commercial, industrial and manufacturing facilities
• High-impact areas: plant rooms, trafficable roof decks
• Areas exposed to high wind abrasion
• Water features, pools and ponds
• Under concrete screed waterproofing of podium decks
• Bridge, street and tunnel construction

Specifications

Components: Comp. A MDI-Prepolymer; Comp. B Polyolamin mixture | Mixing ratio A:B: 1 : 1 by volume | Material consumption: Approx. 1 kg/m2 per 1 mm thickness | Recommended thickness: Minimum 1.0 mm | Gel time at 20 degC: 10 - 15 sec | Tack free time at 20 degC: 15 - 30 sec | Over coat cycle: 0 - 12 hours (without prep and priming) | Application temperature (ambient and substrate): -10 to +50 degC | Spraying material temperature: 65 - 75 degC | VOC content: 0 % | Solids content: 100 % | Colour: Straw / brownish un-pigmented; other colours on request | Density: 0.99 +/- 0.02 g/cm3 | Tensile strength: >= 13 MPa | Elongation at break: 450 % | Hardness: Shore A 89 +/- 5; Shore D 35 +/- 5 | Tear growth resistance: >= 17 N/mm | Taber abrasion: 10 mg (CS17) / 110 mg (H18), 1000 cycles | Fire classification: Class A (ASTM E-108) | Pull off strength: Concrete >= 1.5 N/mm2; Steel >= 4 N/mm2 | Process temperature: Min -40 degC; max wet 50, dry 110 (peak dry 130) degC | Heat conductivity: 0.245 W/m*K | Shelf life: Approx 12 months at +10 to +30 degC

Standards: ASTM E-108 Class A | ASTM D-638 | ASTM D-2240 | ASTM D-4541 | DIN EN ISO 4624