JSW Neosteel Fe 600 is a higher-strength TMT grade listed in the rolling-capability tables of the Vijayanagar works (8-40 mm) and the Dolvi works (8-32 mm, marked 'under development'). The brochure gives its Dolvi chemical, mechanical, bend and re-bend limits.

Key features

• Manufactured from virgin iron ore through the blast furnace route (BF-LHF-Billets-BRM-TMT)
• HYQST technology gives uniform quality across the bar, visible as concentric rings in the cross-section
• Enhanced rib pattern for bonding with cement
• Low sulphur and phosphorous content

Specifications

Grade: Fe 600 | Diameter Range: 8 - 40 mm (Vijayanagar); 8 - 32 mm (Dolvi, under development) | IS 1786 Yield Strength (Min): 600 N/mm2 | IS 1786 Tensile Strength (Min): 660 N/mm2 | IS 1786 UTS/YS Ratio (Min): 1.06 | IS 1786 Elongation (Min): 10 % | JSW Yield Strength (Dolvi Works, Min): 630 N/mm2 | JSW Tensile Strength (Dolvi Works, Min): 690 N/mm2 | JSW UTS/YS Ratio (Dolvi Works, Min): 1.06 | JSW Elongation (Dolvi Works, Min): 10 % | JSW Chemistry (Dolvi Works): C 0.30 % max, P 0.030 % max, S 0.030 % max, S+P 0.060 % max | Bend Test Mandrel Diameter (Dolvi Works, max): 5d up to and incl. 20 mm; 6d over 20 mm | Re-bend Test Mandrel Diameter (Dolvi Works, max): 7d up to and incl. 10 mm; 9d over 10 mm | Weight Tolerance per MT: +/-2 % max | Bundle Weight (Max): 4.5 MT

Standards: IS 1786:2008

Packing: Bundle weight max 4.5 MT (Vijayanagar)