Key features

• Long track record (since 1985)
• Fast reacting spray application
• Application to vertical surfaces without runs
• Monolithic
• Fully bonded
• High water vapour permeability
• Crack bridging
• Solvent and monomeric isocyanate free
• Thermoset
• Remains elastic at low temperatures (Tg approx -35°C)

Applications

• Flat and pitched roofs with UV protection
• Beneath planting or hard landscaping on podium areas
• Beneath XPS insulation or PU foam in inverted or vegetative roofs
• Concrete structures with UV top coat

Specifications

Chemical base: Hybrid polyurethane/polyurea | Density: Part A 1.05 ± 0.03 kg/L; Part B 1.10 ± 0.05 kg/L @25°C | VOC: 1.0 g/L (ISO 11890-2:2020) | Viscosity: Part A 1650 mPas; Part B 1000 mPas @25°C | Shore A hardness: 75 ± 5 (ASTM D2240) | Tensile strength: 8 ~ 10 MPa (ASTM D412) | Elongation at break: ~ 400% (ASTM D412) | Crack bridging: Static A5 (>2.5 mm) EN 1062-7; dynamic 3.2 mm 10 cycles at -26°C (ASTM C1305) | Root penetration: Pass (DIN 4062) | Water penetration: No leakage at 5 bar (DIN 16726) | Mixing ratio: A:B = 100:73 by weight; 100:70 by volume | Product temperature: Part A 70-75°C; Part B 65-70°C | Processing pressure: 130-180 bar | Gel time: 15 ± 3 s | Consumption (waterproofing layer): 1.8-2.4 kg/m² | Dry film thickness: Waterproofing 1.6-2.2 mm; exposed total 1.8-2.4 mm | Shelf life: 12 months | Storage temperature: +10 °C to +30 °C

Standards: Singapore Green Label | JIS A 6021 Type I | ASTM C1305-2016 | DIN 4062 | BBA Roof Certification (2002) | LEED v4 low-emitting materials