Key features

• Long track record (since 1985)
• Solvent free
• Fast reacting spray application
• No sagging on vertical applications
• Monolithic
• Fully bonded
• High water vapour permeability
• Crack bridging
• Thermoset
• Remains elastic at low temperatures (Tg approx -35°C)

Applications

• Flat and pitched roofs with UV top coat
• Beneath planting or hard landscaping on podium areas
• Beneath insulation boards or PU foam in inverted or vegetative roof
• Concrete structures with UV top coat
• Bridge deck / car deck waterproofing

Specifications

Chemical base: Hybrid polyurethane/polyurea | Density: Part A 1.05 ± 0.03 kg/L; Part B 1.10 ± 0.05 kg/L (+25°C) | Viscosity: Part A 1650 mPas; Part B 1000 mPas | Shore A hardness: 75 ± 5 (ASTM D2240) | Tensile strength: ≥ 8 N/mm² (ASTM D412) | Elongation at break: ≥ 400 % (ASTM D412) | Tear strength: > 30 N/mm² (ASTM D624) | Crack bridging: Dynamic - passes (EN 1062-7, B4.2) | Root penetration: Pass (DIN 4062) | Water penetration: No leakage at 5 bar (DIN 16726) | Mixing ratio: A:B = 100:70 by volume; 100:73 by weight | Gel time: 15 ± 3 s at +20°C | Final cure: ~24 hours at +23 °C | Dry film thickness: Non-exposed 1.6-2.2 mm; exposed 1.8-2.2 mm | Shelf life: 12 months | Storage temperature: +10 °C to +30 °C

Standards: Singapore Green Label | JIS A 6021 Type I | ASTM C1305-2016 | DIN 4062 | BBA Roof Certification (2002) | BBA car deck approval (2016) | ETAG-22/0358 bridgedeck (2022) | LEED v4 low-emitting materials