Key features

• Monolithic, no laps, welds or seams
• Fully bonded
• Resistant to puncture and standing water
• Resistant to root penetration
• Thermoset
• Remains elastic at low temperatures
• Can be re-coated
• Excellent crack bridging after a few hours
• No solvent added during construction

Applications

• Balconies and terraces
• Podium decks
• Car park decks
• Railway and bridge decks
• Roofing where no fire-retardant coating is required

Specifications

Chemical base: PU-PUA hybrid | Density: 1.2-1.3 g/cc | Solid content by weight: ≥ 98 % | Root penetration: Pass (CEN/TS 14416) | Tensile strength: ≥ 6 MPa (ASTM D412) | Elongation at break: ≥ 600 % (ASTM D412) | Crack bridging: ≥ 3.2 mm static (EN 1062-7) | Tensile adhesion strength: ≥ 1.5 MPa (ASTM D4541-17) | Tear strength: ≥ 35 N/mm (ASTM D624) | Mixing ratio: A:B = 1:1 by weight | Consumption: ~1.3 kg/m² per 1 mm | Ambient and substrate temperature: +10 °C to +40 °C | Surface dry: ≤ 4 hrs | Dry through: ≤ 24 hrs | Shelf life: 12 months | Storage temperature: 15-25 °C

Standards: CEN/TS 14416

Packing: 20 kg pre-packed working pack (A 10 kg + B 10 kg)